Augustfehn Steels

DURIT VS 140/190/240

Cr-Si-V alloy special steel, with working hardness of 360-550 HB while retaining good impact strength.

Uses: Plates subject to wear, armour plates, lining plates, impact plates, baffle plates, hammers, and grate bars

________________________________________

AUDURIT 26

Special steel with high nickel content and reduced carbon content, to increase toughness under dynamic loading.

Uses: Hammer shafts, knives, doctor blades and special screws

________________________________________

AUDURIT 45A

Uses: Hammers and blow bars

________________________________________

AUDURIT 50A

Ni-Cr-Mo alloy steel, with operating hardness 520-560 HB while retaining good impact strength, and having very good abrasive wear resistance.

Uses: Hammers and blow bars

________________________________________

AUDURIT 60

Ni-Cr-Mo-V alloy steel with working hardness 400-560 HB while retaining good impact strength.

Uses: Hammers and anvils.

________________________________________

AUDURIT 60A

Ni-Cr-Mo-V alloy special steel with high nickel content (~ 3%) and high carbon content, resulting in hardness up to 560 HB, and very high impact strength.

Uses: Hammers and blow bars

________________________________________

AUDURIT 155

Chrome alloy steel (Cr 12-14%) with carbon content approx. 1.6%. Preferred for parts which are subject to highly abrasive conditions.

Uses: Hammers

________________________________________

AUDUCUT 45

Ni-Cr-Mo-V alloy special steel with high nickel content and lower carbon content, for knives and doctor blades subjected to high stresses.

Uses: Knives and doctor blades

________________________________________

MANDURIT 120

Manganese hard steel with Mn content 12-14%, having good resistance to high pressure and heavy impacts. Possibility of surface hardening to hardness of approx. 200-500 HB.

Uses: Hammers and blow bars