Crusher Hammers

Forged Crusher Hammers


Augustfehn’s forged crusher hammers deliver better wear part life over castings and save operators in maintenance costs.

Our crusher hammers are forged from continuous cast blooms and bottom poured ingots strictly from German steel works that meet our tight chemistry specifications. To keep gaseous impurities within limits our steel is vacuum degassed. From there we forge the material crusher hammers, machine details and heat treat for optimal performance. As you can see this is a completely different material from what foundries can deliver.

The real savings go beyond wear part costs.. Customers worldwide report less machine damage from broken hammers and less down time to maintain their mills. Let us help you reduce your mill wear parts cost, decrease downtime and machine damage.

Forged Crusher Hammer Types Available

Forged Crusher Hammer Types

 

Finished Crusher Hammers

Ready to Install Forged Crusher Hammers

 

Hammers for these manufacturers:

Krupp Foerdertechnik, Krupp Polysius, KHD, Hazemag and others.

Material selection

DURIT VS 190

Cr-Si-V alloy special steel, with working hardness of 360-550 HB while retaining good impact strength.



AUDURIT 60

Ni-Cr-Mo-V alloy steel with working hardness 400-560 HB while retaining good impact strength.



AUDURIT 60A

Ni-Cr-Mo-V alloy special steel with high nickel content (c. 3%) and high carbon content, resulting in hardness up to 560 HB, and very high impact strength.



AUDURIT 155

Chrome alloy steel (Cr 12-14%) with carbon content approx. 1.6%. Preferred for parts which are subject to highly abrasive conditions.



MANDURIT 120

Manganese hard steel with Mn content 12-14%, having good resistance to high pressure and heavy impacts. Possibility of surface hardening to hardness of approx. 200-500 HB.

Short delivery time and many wear parts in stock – especially for you!